Hydrogen sorption and hydrogen-induced phase separation in a nearly equiatomic NiZr amorphous alloy

I. Nagy, I. Bakonyi, A. Lovas, E. Tóth-Kádár, K. Tompa, M. Hossó, Á Cziráki, B. Fogarassy

Research output: Article

19 Citations (Scopus)

Abstract

The influence of hydrogen on some physical properties and on the micro-structure of a nearly equiatomic, melt-quenched NiZr amorphous alloy was investigated. Hydrogen absorption from the gas phase at 190 °C and 35-40 atm pressure was measured by weight as a function of the charging time. Considerable hydrogen absorption occurred only for charging times around 10 h and was completed within a few hours. The hydrogen content remained constant for a hydrogen-to-metal ratio of about one for prolonged charging. The room-temperature thermopower changed considerably upon hydriding and a local thermopower probe revealed that the activation time varies considerably along the ribbon length. It was found that, during further heat treatment in a hydrogen gas atmosphere after a hydrogen-to-metal ratio of approximately one was reached, the magnetic state of the amorphous NiZr samples changed progressively from paramagnetic to superparamagnetic. The density and size of the magnetic clusters, which were nickel-rich segregations induced by the hydriding process, were determined by magnetic and scanning transmission electron microscopic measurements. After desorbing hydrogen at elevated temperatures, magnetic measurements indicated the disappearance of the superparamagnetic clusters.

Original languageEnglish
Pages (from-to)283-303
Number of pages21
JournalJournal of the less-common metals
Volume167
Issue number2
DOIs
Publication statusPublished - jan. 1991

ASJC Scopus subject areas

  • Engineering(all)

Fingerprint Dive into the research topics of 'Hydrogen sorption and hydrogen-induced phase separation in a nearly equiatomic NiZr amorphous alloy'. Together they form a unique fingerprint.

  • Cite this