Transalkylation of toluene with cumene over zeolites Y dealuminated in solid-state. Part I. Effect of the alteration of Broensted acidity

V. Mavrodinova, M. Popova, Borbély G. Páł, R. M. Mihályi, Ch Minchev

Research output: Contribution to journalArticle

7 Citations (Scopus)

Abstract

Transalkylation of toluene with cumene was studied over a series of Y zeolites with framework Si/Al ratio of 2.5, 5.6, 12.3 and 21.2 at 453 and 493K. Samples were prepared by progressive dealumination of the parent NH4Y(Si/Al=2.5) zeolite in solid-state with crystalline (NH4)2[SiF6]. It was proved by IR spectroscopy that the replacement of framework aluminum by silicon resulted in an increase in the strength and the thermal stability of the acid sites of Broensted-type. These samples do not contain extra-framework aluminum species. The parent Y zeolite possessing the highest amount of weak Broensted acid sites showed low activity in the transalkylation reaction, and, in addition a considerable amount of reactants and products was found to adsorb on this sample at 453K. The highest cumene conversion was achieved on the sample with Si/Al ratio of 5.6. The balance between the number and strength of the acid centers that assures an optimal activity appears to be disadvantageous in respect to the selectivity. It was demonstrated that the reaction system is very sensitive towards these characteristics influencing not only the activity but also the catalysts' selectivity and stability.

Original languageEnglish
Pages (from-to)181-196
Number of pages16
JournalApplied Catalysis A: General
Volume248
Issue number1-2
DOIs
Publication statusPublished - Aug 8 2003

Fingerprint

Zeolites
Toluene
Acidity
Aluminum
Acids
Catalyst selectivity
Silicon
Infrared spectroscopy
Thermodynamic stability
Crystalline materials
cumene

Keywords

  • Broensted acidity
  • Catalytic performance
  • Cumene-toluene transalkylation
  • Faujasite dealuminated with (NH)[SiF] in solid-state

ASJC Scopus subject areas

  • Catalysis
  • Process Chemistry and Technology

Cite this

Transalkylation of toluene with cumene over zeolites Y dealuminated in solid-state. Part I. Effect of the alteration of Broensted acidity. / Mavrodinova, V.; Popova, M.; Páł, Borbély G.; Mihályi, R. M.; Minchev, Ch.

In: Applied Catalysis A: General, Vol. 248, No. 1-2, 08.08.2003, p. 181-196.

Research output: Contribution to journalArticle

@article{5761776157604c85bc2d1d8af4f9c032,
title = "Transalkylation of toluene with cumene over zeolites Y dealuminated in solid-state. Part I. Effect of the alteration of Broensted acidity",
abstract = "Transalkylation of toluene with cumene was studied over a series of Y zeolites with framework Si/Al ratio of 2.5, 5.6, 12.3 and 21.2 at 453 and 493K. Samples were prepared by progressive dealumination of the parent NH4Y(Si/Al=2.5) zeolite in solid-state with crystalline (NH4)2[SiF6]. It was proved by IR spectroscopy that the replacement of framework aluminum by silicon resulted in an increase in the strength and the thermal stability of the acid sites of Broensted-type. These samples do not contain extra-framework aluminum species. The parent Y zeolite possessing the highest amount of weak Broensted acid sites showed low activity in the transalkylation reaction, and, in addition a considerable amount of reactants and products was found to adsorb on this sample at 453K. The highest cumene conversion was achieved on the sample with Si/Al ratio of 5.6. The balance between the number and strength of the acid centers that assures an optimal activity appears to be disadvantageous in respect to the selectivity. It was demonstrated that the reaction system is very sensitive towards these characteristics influencing not only the activity but also the catalysts' selectivity and stability.",
keywords = "Broensted acidity, Catalytic performance, Cumene-toluene transalkylation, Faujasite dealuminated with (NH)[SiF] in solid-state",
author = "V. Mavrodinova and M. Popova and P{\'a}ł, {Borb{\'e}ly G.} and Mih{\'a}lyi, {R. M.} and Ch Minchev",
year = "2003",
month = "8",
day = "8",
doi = "10.1016/S0926-860X(03)00161-3",
language = "English",
volume = "248",
pages = "181--196",
journal = "Applied Catalysis A: General",
issn = "0926-860X",
publisher = "Elsevier",
number = "1-2",

}

TY - JOUR

T1 - Transalkylation of toluene with cumene over zeolites Y dealuminated in solid-state. Part I. Effect of the alteration of Broensted acidity

AU - Mavrodinova, V.

AU - Popova, M.

AU - Páł, Borbély G.

AU - Mihályi, R. M.

AU - Minchev, Ch

PY - 2003/8/8

Y1 - 2003/8/8

N2 - Transalkylation of toluene with cumene was studied over a series of Y zeolites with framework Si/Al ratio of 2.5, 5.6, 12.3 and 21.2 at 453 and 493K. Samples were prepared by progressive dealumination of the parent NH4Y(Si/Al=2.5) zeolite in solid-state with crystalline (NH4)2[SiF6]. It was proved by IR spectroscopy that the replacement of framework aluminum by silicon resulted in an increase in the strength and the thermal stability of the acid sites of Broensted-type. These samples do not contain extra-framework aluminum species. The parent Y zeolite possessing the highest amount of weak Broensted acid sites showed low activity in the transalkylation reaction, and, in addition a considerable amount of reactants and products was found to adsorb on this sample at 453K. The highest cumene conversion was achieved on the sample with Si/Al ratio of 5.6. The balance between the number and strength of the acid centers that assures an optimal activity appears to be disadvantageous in respect to the selectivity. It was demonstrated that the reaction system is very sensitive towards these characteristics influencing not only the activity but also the catalysts' selectivity and stability.

AB - Transalkylation of toluene with cumene was studied over a series of Y zeolites with framework Si/Al ratio of 2.5, 5.6, 12.3 and 21.2 at 453 and 493K. Samples were prepared by progressive dealumination of the parent NH4Y(Si/Al=2.5) zeolite in solid-state with crystalline (NH4)2[SiF6]. It was proved by IR spectroscopy that the replacement of framework aluminum by silicon resulted in an increase in the strength and the thermal stability of the acid sites of Broensted-type. These samples do not contain extra-framework aluminum species. The parent Y zeolite possessing the highest amount of weak Broensted acid sites showed low activity in the transalkylation reaction, and, in addition a considerable amount of reactants and products was found to adsorb on this sample at 453K. The highest cumene conversion was achieved on the sample with Si/Al ratio of 5.6. The balance between the number and strength of the acid centers that assures an optimal activity appears to be disadvantageous in respect to the selectivity. It was demonstrated that the reaction system is very sensitive towards these characteristics influencing not only the activity but also the catalysts' selectivity and stability.

KW - Broensted acidity

KW - Catalytic performance

KW - Cumene-toluene transalkylation

KW - Faujasite dealuminated with (NH)[SiF] in solid-state

UR - http://www.scopus.com/inward/record.url?scp=0041923836&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0041923836&partnerID=8YFLogxK

U2 - 10.1016/S0926-860X(03)00161-3

DO - 10.1016/S0926-860X(03)00161-3

M3 - Article

AN - SCOPUS:0041923836

VL - 248

SP - 181

EP - 196

JO - Applied Catalysis A: General

JF - Applied Catalysis A: General

SN - 0926-860X

IS - 1-2

ER -