The soft magnetic properties and temperature stability of Co-Fe-Zr-B metallic glasses

J. Bednarčík, J. Kováč, S. Roth, J. Füzer, P. Kollár, L. K. Varga, H. Franz

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

In the present work multicomponent Co-based alloys with nominal composition Co72-xFexZr8B20 (x = 10, 15, and 20 at.%) were synthesized by single-roller melt-spinning. The measurement of coercivity, Hc, reveals the soft magnetic behavior of investigated alloys. The value of Hc increases from 23 A/m for alloy with x = 10 at.% up to 32 A/m for alloy with x = 20 at.%. Further it was found that crystallization temperature of as-quenched alloys slightly varies with iron content and lays between 605 and 625°C. From the temperature dependence of magnetization it follows that partial substitution of cobalt by iron has positive influence on the Curie temperature of amorphous phase, T cam, which increases from 300°C up to 462°C for alloy with x = 10 at.% and x = 20 at.%, respectively.

Original languageEnglish
Pages (from-to)83-86
Number of pages4
JournalActa Physica Polonica A
Volume113
Issue number1
DOIs
Publication statusPublished - Jan 2008

    Fingerprint

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Cite this