The processing of Mg-Ti for hydrogen storage; Mechanical milling and plasma synthesis

G. Çakmak, Z. Károly, I. Mohai, T. Öztürk, J. Szépvölgyi

Research output: Contribution to journalArticle

17 Citations (Scopus)

Abstract

A study was carried out into the processing of Mg-10 vol.% Ti powder mixture for hydrogen storage purposes. Two processing routes were evaluated; mechanical milling and plasma synthesis. Mechanical milling, carried out with a high speed planetary mill, yielded a particulate structure made up of large Mg agglomerates, 90-100 μm, with embedded Ti fragments of approx. 1 μm in size with a uniform distribution. Mg agglomerates were made up of coherently diffracting volumes that were less than 50 nm in size. Plasma processing was carried out with an RF plasma torch of 25-27 kW applied power, the powder mixtures fed with 1-3 g/min axially into the torch. The mixture Mg-10 vol.% Ti after plasma processing comprised Mg powders which were extremely fine, <100 nm. Ti occurred as separate particles mixed with Mg nanopowders. The powders had a coherently diffracting volumes that were comparable to the size of the particles themselves indicating that the plasma processing yields relatively defect free crystals. The formation of the nano-size particulate structures is evaluated with regard to their possible implications on the hydrogenation of Mg-Ti alloys.

Original languageEnglish
Pages (from-to)10412-10418
Number of pages7
JournalInternational Journal of Hydrogen Energy
Volume35
Issue number19
DOIs
Publication statusPublished - Oct 1 2010

Keywords

  • Hydrogen storage
  • Mechanical milling
  • Mg nanopowders
  • Plasma synthesis

ASJC Scopus subject areas

  • Renewable Energy, Sustainability and the Environment
  • Fuel Technology
  • Condensed Matter Physics
  • Energy Engineering and Power Technology

Fingerprint Dive into the research topics of 'The processing of Mg-Ti for hydrogen storage; Mechanical milling and plasma synthesis'. Together they form a unique fingerprint.

  • Cite this