Synthesis of thermoplastic composites from carbon fibers treated by plasma immersion ion implantation (PIII)

L. L G Silva, L. G. Alves, A. L. Santos, E. C. Botelho, A. Tóth, M. Ueda

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

This paper deals with synthesis of thermoplastic composites from CFs treated by PIII processing at different treatment times, 2, 5, 10 and 15 min. The characterization of CFs samples was carried out using the following analyses: SEM, XPS, AFM and Raman spectroscopy. After this previous characterization of the CF reinforcement, the thermoplastic laminate was produced using hot compression molding technology. The laminate was characterized by Interlaminar shear test (ILSS) and SEM analysis. After the PIII treatments there was an increase in the surface roughness and an introduction of the polar groups on the carbon fiber surface. These modifications enhance the adhesion in the composites interface as confirmed by ILSS tests that show up to double increase in the shear strenght in comparison to composites obtained from untreated CFs.

Original languageEnglish
Title of host publicationECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials
PublisherEuropean Conference on Composite Materials, ECCM
ISBN (Print)9788888785332
Publication statusPublished - 2012
Event15th European Conference on Composite Materials: Composites at Venice, ECCM 2012 - Venice, Italy
Duration: Jun 24 2012Jun 28 2012

Other

Other15th European Conference on Composite Materials: Composites at Venice, ECCM 2012
CountryItaly
CityVenice
Period6/24/126/28/12

Fingerprint

Ion implantation
Thermoplastics
Carbon fibers
Plasmas
Laminates
Composite materials
Scanning electron microscopy
Compression molding
Hot pressing
Raman spectroscopy
Reinforcement
Adhesion
X ray photoelectron spectroscopy
Surface roughness
Processing
carbon fiber

Keywords

  • Carbon fibers
  • Interlaminar shear strenght
  • Plasma immersion ion implantation
  • Thermoplastic composites

ASJC Scopus subject areas

  • Ceramics and Composites

Cite this

Silva, L. L. G., Alves, L. G., Santos, A. L., Botelho, E. C., Tóth, A., & Ueda, M. (2012). Synthesis of thermoplastic composites from carbon fibers treated by plasma immersion ion implantation (PIII). In ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials European Conference on Composite Materials, ECCM.

Synthesis of thermoplastic composites from carbon fibers treated by plasma immersion ion implantation (PIII). / Silva, L. L G; Alves, L. G.; Santos, A. L.; Botelho, E. C.; Tóth, A.; Ueda, M.

ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. European Conference on Composite Materials, ECCM, 2012.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Silva, LLG, Alves, LG, Santos, AL, Botelho, EC, Tóth, A & Ueda, M 2012, Synthesis of thermoplastic composites from carbon fibers treated by plasma immersion ion implantation (PIII). in ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. European Conference on Composite Materials, ECCM, 15th European Conference on Composite Materials: Composites at Venice, ECCM 2012, Venice, Italy, 6/24/12.
Silva LLG, Alves LG, Santos AL, Botelho EC, Tóth A, Ueda M. Synthesis of thermoplastic composites from carbon fibers treated by plasma immersion ion implantation (PIII). In ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. European Conference on Composite Materials, ECCM. 2012
Silva, L. L G ; Alves, L. G. ; Santos, A. L. ; Botelho, E. C. ; Tóth, A. ; Ueda, M. / Synthesis of thermoplastic composites from carbon fibers treated by plasma immersion ion implantation (PIII). ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. European Conference on Composite Materials, ECCM, 2012.
@inproceedings{8ffd092c0a3c439e9ae26781a1e9317c,
title = "Synthesis of thermoplastic composites from carbon fibers treated by plasma immersion ion implantation (PIII)",
abstract = "This paper deals with synthesis of thermoplastic composites from CFs treated by PIII processing at different treatment times, 2, 5, 10 and 15 min. The characterization of CFs samples was carried out using the following analyses: SEM, XPS, AFM and Raman spectroscopy. After this previous characterization of the CF reinforcement, the thermoplastic laminate was produced using hot compression molding technology. The laminate was characterized by Interlaminar shear test (ILSS) and SEM analysis. After the PIII treatments there was an increase in the surface roughness and an introduction of the polar groups on the carbon fiber surface. These modifications enhance the adhesion in the composites interface as confirmed by ILSS tests that show up to double increase in the shear strenght in comparison to composites obtained from untreated CFs.",
keywords = "Carbon fibers, Interlaminar shear strenght, Plasma immersion ion implantation, Thermoplastic composites",
author = "Silva, {L. L G} and Alves, {L. G.} and Santos, {A. L.} and Botelho, {E. C.} and A. T{\'o}th and M. Ueda",
year = "2012",
language = "English",
isbn = "9788888785332",
booktitle = "ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials",
publisher = "European Conference on Composite Materials, ECCM",

}

TY - GEN

T1 - Synthesis of thermoplastic composites from carbon fibers treated by plasma immersion ion implantation (PIII)

AU - Silva, L. L G

AU - Alves, L. G.

AU - Santos, A. L.

AU - Botelho, E. C.

AU - Tóth, A.

AU - Ueda, M.

PY - 2012

Y1 - 2012

N2 - This paper deals with synthesis of thermoplastic composites from CFs treated by PIII processing at different treatment times, 2, 5, 10 and 15 min. The characterization of CFs samples was carried out using the following analyses: SEM, XPS, AFM and Raman spectroscopy. After this previous characterization of the CF reinforcement, the thermoplastic laminate was produced using hot compression molding technology. The laminate was characterized by Interlaminar shear test (ILSS) and SEM analysis. After the PIII treatments there was an increase in the surface roughness and an introduction of the polar groups on the carbon fiber surface. These modifications enhance the adhesion in the composites interface as confirmed by ILSS tests that show up to double increase in the shear strenght in comparison to composites obtained from untreated CFs.

AB - This paper deals with synthesis of thermoplastic composites from CFs treated by PIII processing at different treatment times, 2, 5, 10 and 15 min. The characterization of CFs samples was carried out using the following analyses: SEM, XPS, AFM and Raman spectroscopy. After this previous characterization of the CF reinforcement, the thermoplastic laminate was produced using hot compression molding technology. The laminate was characterized by Interlaminar shear test (ILSS) and SEM analysis. After the PIII treatments there was an increase in the surface roughness and an introduction of the polar groups on the carbon fiber surface. These modifications enhance the adhesion in the composites interface as confirmed by ILSS tests that show up to double increase in the shear strenght in comparison to composites obtained from untreated CFs.

KW - Carbon fibers

KW - Interlaminar shear strenght

KW - Plasma immersion ion implantation

KW - Thermoplastic composites

UR - http://www.scopus.com/inward/record.url?scp=84903954319&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84903954319&partnerID=8YFLogxK

M3 - Conference contribution

AN - SCOPUS:84903954319

SN - 9788888785332

BT - ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials

PB - European Conference on Composite Materials, ECCM

ER -