Sub-micrometre holotomographic characterisation of the effects of solution heat treatment on an AlMg7.3Si3.5 alloy

D. Tolnai, G. Requena, P. Cloetens, J. Lendvai, H. P. Degischer

Research output: Contribution to journalArticle

12 Citations (Scopus)

Abstract

A strip cast AlMg7.3Si3.5 alloy is investigated by sub-micrometre holotomographic analysis achieving a voxel size of (60nm) 3 by cone beam magnification of the focused synchrotron beam using Kirkpatrick-Baez mirrors. The three-dimensional microstructure of the same specimen volume in the as-cast state is compared with that after exposure to 540°C for 30min resolving microstructural features down to 180nm. The three-dimensional analysis of the architecture of the eutectic Mg 2Si and the Fe-aluminides reveals how the as-cast microstructure changes during the solution treatment. The alloy in the as-cast condition contains a highly interconnected seaweed-like Mg 2Si eutectic. The level of three-dimensional interconnectivity of the Mg 2Si eutectic phase decreases by only partial disintegration during the heat treatment correcting the two-dimensional metallographic impression of isolated round particles. Statistical analyses of the particle distribution, sphericity, mean curvatures and Gaussian curvatures describe quantitatively the architectural changes of the Mg 2Si phase. This explains the decrease of the high temperature strength of the alloy by the solution treatment tested in hot compression.

Original languageEnglish
Pages (from-to)214-221
Number of pages8
JournalMaterials Science and Engineering A
Volume550
DOIs
Publication statusPublished - Jul 30 2012

Keywords

  • Aluminium alloys
  • Cast Al-Mg-Si alloys
  • Coarsening
  • Mechanical characterisation
  • Synchrotron tomography

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Sub-micrometre holotomographic characterisation of the effects of solution heat treatment on an AlMg7.3Si3.5 alloy'. Together they form a unique fingerprint.

  • Cite this