Microstructure decomposition and unique mechanical properties in an ultrafine-grained Al-Zn alloy processed by high-pressure torsion

A. Baris, N. Q. Chinh, R. Z. Valiev, T. G. Langdon

Research output: Contribution to journalArticle


An ultrafine-grained (UFG) Al-30wt.%Zn alloy was processed by high-pressure torsion (HPT) and then the mechanical and microstructural properties were investigated using depth-sensing indentations (DSI), focused ion beam (FIB), scanning electron microscopy (SEM) and differential scanning calorimetry (DSC). Emphasis was placed on the microstructure changes due to HPT processing as well as the effects of grain boundaries and the unusually high strain rate sensitivity. The deformation characteristics are explained by the formation of a Zn-rich phase which wets the Al/Al grain boundaries and enhances the role of grain boundary sliding in this UFG alloy. The occurrence of intensive grain boundary sliding in this UFG alloy at room temperature was also demonstrated by deforming micro-pillars. It is shown that, as a result of grain boundary sliding, the plastic deformation process of the UFG samples remains stable even at the micro-scale without the intermittent flow and detrimental strain avalanches which are an inherent feature of micro-size conventional crystals. This result illustrates the advantage of using UFG materials for effective applications in micro-devices.

Original languageEnglish
Pages (from-to)251-258
Number of pages8
JournalKovove Materialy
Issue number4
Publication statusPublished - Jan 1 2015



  • Grain boundary sliding
  • Indentation
  • Micro-pillars
  • Strain rate sensitivity
  • Ultrafine grains

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Cite this