Distortion scattering due to guinier-preston zones in AlAg

T. Ungár, Ph A. Dubey, G. Kostorz

Research output: Contribution to journalArticle

8 Citations (Scopus)

Abstract

For a decomposing Al-3 at.%Ag alloy the mismatch of Guinier-Preston zones was determined from high-resolution measurements of the diffuse X-ray scattering near the 222 Bragg reflection. It was found that the mismatch of the Guinier-Preston zones is largest directly after quenching and decreases monotonically with ageing time. In the temperature range from 110 to 200°C the rate of mismatch reduction increases with increasing temperature.

Original languageEnglish
Pages (from-to)2583-2586
Number of pages4
JournalActa Metallurgica et Materialia
Volume38
Issue number12
DOIs
Publication statusPublished - 1990

Fingerprint

Scattering
X ray scattering
Quenching
Aging of materials
Temperature

ASJC Scopus subject areas

  • Engineering(all)

Cite this

Distortion scattering due to guinier-preston zones in AlAg. / Ungár, T.; Dubey, Ph A.; Kostorz, G.

In: Acta Metallurgica et Materialia, Vol. 38, No. 12, 1990, p. 2583-2586.

Research output: Contribution to journalArticle

Ungár, T. ; Dubey, Ph A. ; Kostorz, G. / Distortion scattering due to guinier-preston zones in AlAg. In: Acta Metallurgica et Materialia. 1990 ; Vol. 38, No. 12. pp. 2583-2586.
@article{abf78e40a6ce4d8595eccd71790beb8b,
title = "Distortion scattering due to guinier-preston zones in AlAg",
abstract = "For a decomposing Al-3 at.{\%}Ag alloy the mismatch of Guinier-Preston zones was determined from high-resolution measurements of the diffuse X-ray scattering near the 222 Bragg reflection. It was found that the mismatch of the Guinier-Preston zones is largest directly after quenching and decreases monotonically with ageing time. In the temperature range from 110 to 200°C the rate of mismatch reduction increases with increasing temperature.",
author = "T. Ung{\'a}r and Dubey, {Ph A.} and G. Kostorz",
year = "1990",
doi = "10.1016/0956-7151(90)90270-Q",
language = "English",
volume = "38",
pages = "2583--2586",
journal = "Acta Materialia",
issn = "1359-6454",
publisher = "Elsevier Limited",
number = "12",

}

TY - JOUR

T1 - Distortion scattering due to guinier-preston zones in AlAg

AU - Ungár, T.

AU - Dubey, Ph A.

AU - Kostorz, G.

PY - 1990

Y1 - 1990

N2 - For a decomposing Al-3 at.%Ag alloy the mismatch of Guinier-Preston zones was determined from high-resolution measurements of the diffuse X-ray scattering near the 222 Bragg reflection. It was found that the mismatch of the Guinier-Preston zones is largest directly after quenching and decreases monotonically with ageing time. In the temperature range from 110 to 200°C the rate of mismatch reduction increases with increasing temperature.

AB - For a decomposing Al-3 at.%Ag alloy the mismatch of Guinier-Preston zones was determined from high-resolution measurements of the diffuse X-ray scattering near the 222 Bragg reflection. It was found that the mismatch of the Guinier-Preston zones is largest directly after quenching and decreases monotonically with ageing time. In the temperature range from 110 to 200°C the rate of mismatch reduction increases with increasing temperature.

UR - http://www.scopus.com/inward/record.url?scp=0025539126&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0025539126&partnerID=8YFLogxK

U2 - 10.1016/0956-7151(90)90270-Q

DO - 10.1016/0956-7151(90)90270-Q

M3 - Article

AN - SCOPUS:0025539126

VL - 38

SP - 2583

EP - 2586

JO - Acta Materialia

JF - Acta Materialia

SN - 1359-6454

IS - 12

ER -